TPU-188 Duraplate Acrylic Urethane

Home :: Heavy Duty/Industrial :: TPU-188 Duraplate Acrylic Urethane
TPU-188 Duraplate Acrylic Urethane
View detailed images (1)
TPU-188 Duraplate Acrylic Urethane

Product Downloads

Download Technical Data
Download MSDS
Download MSDS Part B

DURAPLATE ACRYLIC URETHANE

A test patch is recommended

TPU-188 Duraplate Acrylic Urethane is a high quality acrylic polyurethane with quick drying times. TPU- 188 has very good exterior gloss and color retention. This type of polyurethane is the most widely used for commercial/industrial flooring, and decorative concrete in a commercial setting. Available in Lt., Deep and Clear Tint bases, tintable wit hindustrial tints as will as Bronze, Black and Clear Coat Standard gloss is high. Tinted bases may exhibit lower gloss, depending on colorant level, and should be taken into consideration.

TPU-188 is Best Used for

  • Commercial Industrial Flooring

    Commercial Industrial Flooring

  • Decorative Concrete

    Decorative Concrete
SKU TPU-188
Carrier Water
Compliance A.I.M
Primer None required
Usage on Unpainted Surfaces Concrete Floors
Concrete Walls
Concrete Drives
Garage Floors
Block Walls
Use to Recoat Polyurethane Porch and Deck Enamel
Epoxies
 
Our price:
Quantity
Add to comparison list
Compare product with:

Technical Information

Physical Data:

INFORMATION VARIES WITH COLOR. DATA SHOWN IS FOR WHITE.
Weight per Gallon 9.78 lbs.
solids by volume 37.5%
Solids content by weight 45.1%
Recommended dry film thickness 2-3 mils.
Recommended wet film thickness 4-6 mils.
Minimum time before recoat Dry to touch about 60 mins for spray, 4-6 hours for roller application
Maximum time before recoat None, scuff sand if re-coating after 48 hours
Full Cure 5 days @ 75F
Flash point 53F
VOC As supplied
Shelf life (cool and dry) Minimum 12 months in unopened container
Mix Ratio 4 to 1 1700 catalyst rated flammable
Pot life 6-8 hours @ 75 F
Thinning Not recommended.

Packaging:

TPU-188 is a two package catalyzed system, available in 1 gallon cans and 5 gallon pails. Both 1 and 5 gallon containers are short filled to accommodate tint and catalyst (bases) or catalyst only (standard colors). TPU-188 is sold as a "kit" part A (base compound), and part B (catalyst) are packaged separately.

Principal Characteristics:

  • Excellent gloss and color retention
  • High hiding & fast drying
  • Apply with roller or spray, touch up with brush
  • Excellent water, Chemical and impact resistance
  • Excellent resistance to brake and transmission fluid
  • Interior and exterior use
  • Excellent hardness and flexibility
  • Excellent "wrap" with electrostatic spray

Usage Information

Preparation:

For most applications requiring color, an epoxy basecoat or primer is preferred to obtain optimum adhesion to the surface. Surface to be coated should be clean, dry and have a profile similar to 180-220 girt sandpaper. On new cement overlays, no other preparation is necessary other than to insure the surface is clean, dry and contaminant free. Over stamped overlays, make sure all form release, and loose color release is removed from the surface. Overlays must be completely dry before coating.

Application:

Application by conventional spray, or airless spray is recommended. May also be applied with a brush or roller. For roller application, use a 3/16" nap mohair cover with phenolic core, apply slowly to avoid air entrainment. Lightly back roll after 2-5 minutes to remove air bubbles caused by permanent displacement.

Instructions for Use:

This is a two component system. Part A is pigmented and must be thoroughly mixed before the addition of the catalyst. The two components must be mixed in a ration of 4 parts (A) to part (B) - then mixed completely before application. If the temperature is below 50 F, it may be necessary to add solvents to obtain application viscosity. DO NOT APPLY when surface temperature is about 90 degrees F. lap marking and poor adhesion may result. This results in lower sag resistance, slower cure and thinner films. If thinning is required, add thinner after mixing the components. Very good mechanical mixing of base, catalyst and thinner is essential.